Filamento Polymaker HT-PLA-GF 1,75 mm, 1 kg, colore Blue (PA18004)

Polymaker HT-PLA-GF is a glass fiber reinforced PLA filament engineered for higher heat resistance than standard PLA. Its glass fiber content increases stiffness and dimensional stability, while the HT-PLA base allows for annealing to achieve a heat deflection temperature of 100°C. The natural grey color has a matte, technical appearance ideal for functional parts, jigs, and fixtures that require better thermal performance than conventional PLA.

Highlights

• High-temperature PLA with glass fiber reinforcement for improved rigidity
• Annealing capability raises HDT to 100°C for heat-resistant applications
• Low warping and good printability on open-frame printers
• 1.75 mm diameter, 1 kg net weight spool

In daily use

Printing with HT-PLA-GF is similar to standard PLA, but the glass fiber content makes the filament more abrasive. A hardened steel or ruby nozzle is recommended to prevent wear. Parts printed with this material can be annealed in an oven to increase their heat resistance, making them suitable for applications that would normally deform standard PLA, such as under-hood automotive components or electronics enclosures.

Full specifications

• Material: High-Temperature Glass Fiber Reinforced Polylactic Acid (HT-PLA-GF)
• Filament Diameter: 1.75 mm
• Net Filament Weight: 1 kg
• Color: Natural Grey
• Recommended Print Temperature: 200 - 230 °C
• Recommended Bed Temperature: 25 - 60 °C
• Recommended Print Speed: 30 - 60 mm/s
• Density: 1.25 g/cm³
• Heat Deflection Temperature (HDT): 100 °C (Annealed)
• Glass Transition Temperature (Tg): 60 °C (Unannealed)
• Tensile Strength: 60 MPa
• Flexural Modulus: 4000 MPa
• Impact Strength (Izod): 5 kJ/m²
• Recommended Nozzle Material: Hardened Steel or Ruby Nozzle
• Spool Diameter: 200 mm
• Spool Width: 65 mm
• Spool Hub Diameter: 55 mm

Final note

For applications requiring higher temperature resistance than standard PLA, HT-PLA-GF offers a practical solution with the added stiffness of glass fiber reinforcement.