HellermannTyton 435-00083 Resina epossidica bicomponente, verde, 12,5 kg kit

The HellermannTyton 435-00083 is a two-component epoxy resin formulated for electrical insulation, potting, sealing, and cable jointing. Its 1:1 mixing ratio by volume simplifies preparation, while the green colour provides clear visual confirmation of mixing and coverage. Unlike many resins that require precise weighing, this system allows reliable field mixing with simple volumetric measures.

Highlights

• Two-component epoxy resin for electrical insulation and sealing
• Convenient 1:1 mixing ratio by volume
• Green colour for easy mixing verification
• Halogen-free formulation
• Good chemical resistance to water, oils, fuels, alkalis, and diluted acids

In daily use

The resin offers a pot life of approximately 30 minutes at 23°C, allowing sufficient working time for careful application. Full cure is achieved in about 24 hours at room temperature. Once cured, it provides a hard, durable finish with a Shore D hardness of approximately 75 and excellent dielectric strength exceeding 20 kV/mm.

Full specifications

• Product type: Two-component epoxy resin
• Material: Epoxy resin
• Colour (mixed): Green
• Mixing ratio (resin:hardener): 1:1 by volume
• Pot life at 23°C: Approx. 30 minutes
• Curing time at 23°C: Approx. 24 hours (full cure)
• Dielectric strength: >20 kV/mm
• Operating temperature range: -20°C to +90°C
• Hardness (Shore D): Approx. 75
• Viscosity (mixed at 23°C): Approx. 1500 mPa·s
• Density (mixed at 23°C): Approx. 1.15 g/cm³
• Water absorption (24h): <0.1%
• Chemical resistance: Excellent against water, oils, fuels, alkalis, diluted acids
• UV resistance: Good
• Halogen-free: Yes
• Shelf life: 36 months (unopened, stored at 5-25°C)
• Packaging type: Bulk canister / Kit
• Safety features: Non-toxic after curing, low exotherm
• Standards compliance: RoHS, REACH